Molecular Sieve 3A |
| |
|
| |
Formula: 0.4K2O - 0.6Na2O - Al2O3 - 2.0SiO2 - 4.5H2O
Technical data:
Appearance ---------------- sphere
Size ------------------------- 1.7-2.5 mm, 3.0-5.0 mm
Size ratio up to grade ----- >=96%
Bulk density ---------------- >=600G/L
Wear ratio ------------------ <=0.20%
Crushing strength ---------- >=45P, 60P
Static H2O adsorption ------ >=20%
Moisture content ------------ <=1.5%
|
| |
Molecular Sieve 4A
Formula: Na2O - Al2O3 - 2.0SiO2 - 4.5H2O
Technical data:
Appearance ---------------- sphere
Size ------------------------- 1.7-2.5 mm, 3.0-5.0 mm
Size ratio up to grade ----- >=96%
Bulk density ---------------- >=600G/L
Wear ratio ------------------ <=0.20%
Crushing strength ---------- >=60P, 70P
Static H2O adsorption ------ >=20.5%
Methane adsorption -------- >=16
Moisture content ------------ <=1.5%
BACK TO TOP |
| |
Molecular Sieve 5A
Formula: 0.70CaO - 0.3Na2O - Al2O3 - 2.0SiO2 - 4.5H2O
Technical data:
Appearance ---------------- sphere
Size ------------------------- 2.0-3.0 mm, 3.0-5.0 mm
Size ratio up to grade ----- >=96%
Bulk density ---------------- >=600G/L
Wear ratio ------------------ <=0.20%
Crushing strength ---------- >=30P, 60P
Static H2O adsorption ------ >=21.5%
N-hexane adsorption ------- >=14%
Moisture content ------------ <=1.5%
|
| |
BACK TO TOP |
| |
Molecular Sieve 13X
Formula: Na2O - Al2O3 - 2.45SiO2 - 6.0H2O
Technical data:
Appearance ---------------- sphere
Size ------------------------- 1.0-1.6 mm, 3.0-5.0 mm
Size ratio up to grade ----- >=96%
Bulk density ---------------- >=600G/L
Wear ratio ------------------ <=0.20%
Crushing strength ---------- >=10P, 60P
Static H2O adsorption ------ >=20%
CO2 air disposal ------------ >= 14%
Moisture content ------------ <=1.5%
BACK TO TOP |
| |
IG Desiccant
IG Desiccant can deeply co-adsorb the resident moisture and organics in Insulating Glass, keep the IG clear and transparent even at very low temperature.
Technical data:
Appearance ---------------- sphere
Size ------------------------- 0.5-1.0 mm, 1.0-1.6 mm, 1.5-2.0 mm
Size ratio up to grade ----- >=98%
Bulk density ---------------- >=740G/L
Wear ratio ------------------ <=0.20%
Crushing strength ---------- >=7P, 14P, 20P
Static H2O adsorption ----- >=19%
H2O adsorptive speed ----- >=0.60mg/g-min
Nitrogen adsorption -------- <=2.0mg/g
Organic adsorption --------- Yes, No (tow kinds)
Dew point -------------------<=-60oC
Moisture content ------------ <=1.5%
|
| |